Thanks to its broad usable optical spectrum and outstanding attenuation performance, FullBand® Plus Low Loss Single-mode Fibre is the optimum choice that supports various applications such as Ethernet, Internet Protocol (IP), Asychronous Transfer Mode (ATM), Synchronous Distribution Network (SDH) and Wavelength Division Multiplexing (WDM). FullBand® Plus Low Loss Singlemode Fibre provides wider bandwidth and much lower signal attenuation for backbone, metropolitan area and access networks.
FullBand? Plus Low Loss Single-mode Fibre
YOFC FullBand? Plus Low Loss Single-mode Fibre is designed specially for optical transmission systems* which operates over the entire wavelength window from 1260 nm to 1625 nm. By suppressing the water peak that occurs near 1383 nm in conventional single mode fibre due to hydroxyl (OH-) ions absorption, FullBand? Plus Fibre is able to open E-band (1360 to 1460nm ) for operation, and consequently provides 100 nm more usable wavelengths. FullBand? Plus Fibre is effectively optimized for much lower attenuation level across the entire wavelength window from 1260 nm up to 1625 nm.
Details
Specification
Documents
Applications
百度 而据未来可栖消息称，链家集团董事长左晖认为，未来北京会有1000万人租房，按人均20平米左右计算，北京需要的租房面积将达两亿平米。
Product standards
- YOFC FullBand? Plus fibre complies with or even exceeds the ITU-T Recommendation G.652.D and the IEC 60793-2-50 type B1.3 Optical Fibre Specification.
- YOFC tightens many parameters of fibre products.
Characteristics
? Designed for operation over the full optical spectrum from 1260-1625 nm, and hence the transmission capacity is increased
? Much lower attenuation over the full optical spectrum from 1260 nm to 1625 nm, which meet the demand of extended long distance transmission
? Outstanding optical performance supporting high-speed transmission technologies such as DWDM and CWDM
? Being compatible with existing 1310 nm equipment
? Good protection and excellent strip force stability
? Accurate geometrical parameters that insure low splicing loss and high splicing efficiency
Specifications
|
Characteristics |
Conditions |
Speci?ed values |
Units |
|
|---|---|---|---|---|
|
Optical Characteristics |
||||
|
? ? Attenuation |
1310nm |
≤0.32 |
[dB/km] |
|
|
1383nm(after H2-aging) |
≤0.31 |
[dB/km] |
||
|
1550nm |
≤0.18 |
[dB/km] |
||
|
1625nm |
≤0.20 |
[dB/km] |
||
|
Attenuation vs. Wavelength Max. α di?erence |
1285-1330nm,?in reference to 1310nm |
≤0.03 |
[dB/km] |
|
|
1525-1575nm, in reference to 1550nm |
≤0.02 |
[dB/km] |
||
|
? Dispersion Coe?cient |
1285-1340nm |
-3.5 to 3.5 |
[ps/(nm·km)] |
|
|
1550nm |
≤18 |
[ps/(nm·km)] |
||
|
1625nm |
≤22 |
[ps/(nm·km)] |
||
|
Zero Dispersion Wavelength(λ0) |
-- |
1300-1324 |
[nm] |
|
|
Zero Dispersion Slope(S0) |
-- |
≤0.092 |
[ps/(nm2·km)] |
|
|
Typical Value |
-- |
0.086 |
[ps/(nm2·km)] |
|
|
PMD |
Maximum Individual Fibre |
-- |
≤0.1 |
[ps/√km] |
| Link Design Value（M=20，Q=0.01%) |
-- |
≤0.06 |
[ps/√km] |
|
| Typical Value |
-- |
0.04 |
[ps/√km] |
|
|
Cable Cuto? Wavelength (λCC) |
-- |
≤1260 |
[nm] |
|
|
Mode Field Diameter（MFD） |
1310nm |
8.7-9.5 |
[μm] |
|
|
1550nm |
9.8-10.8 |
[μm] |
||
|
E?ective Group Index of Refraction（Ne??） |
1310nm |
1.466 |
-- |
|
|
1550nm |
1.467 |
-- |
||
|
Point Discontinuities |
1310nm |
≤0.05 |
[dB] |
|
|
1550nm |
≤0.05 |
[dB] |
||
|
Geometrical Characteristics |
||||
|
Cladding Diameter |
-- |
125.0±0.7 |
[μm] |
|
|
Cladding Non-Circularity |
-- |
≤1.0 |
[%] |
|
|
Coating Diameter |
-- |
235-245 |
[μm] |
|
|
Coating-Cladding Concentricity Error |
-- |
≤12.0 |
[μm] |
|
|
Coating Non-Circularity |
-- |
≤6.0 |
[%] |
|
|
Core-Cladding Concentricity Error |
-- |
≤0.6 |
[μm] |
|
|
Curl(radius) |
-- |
≥4 |
[m] |
|
|
Delivery Length |
-- |
Up to 50.4 |
[km/reel] |
|
|
Environmental Characteristics |
1310nm, 1550nm & 1625nm |
|||
|
Temperature Dependence Induced Attenuation |
-60℃ to +85℃ |
≤0.05 |
[dB/km] |
|
|
Temperature-Humidity Cycling Induced Attenuation |
-10°C to +85°C, 98% RH |
≤0.05 |
[dB/km] |
|
|
Watersoak Dependence Induced Attenuation |
23°C，for 30 days |
≤0.05 |
[dB/km] |
|
|
Damp Heat Dependence Induced Attenuation |
85°C and 85% RH，for 30 days |
≤0.05 |
[dB/km] |
|
|
Dry Heat Aging |
85℃,?for 30 days |
≤0.05 |
[dB/km] |
|
|
Mechanical Speci?cation |
||||
|
? Proof Test |
-- |
≥9.0 |
[N] |
|
|
-- |
≥1.0 |
[%] |
||
|
-- |
≥100 |
[kpsi] |
||
|
Macro-bend Induced Attenuation |
100 Turns Around a Mandrel of 30 mm Radius |
1625nm |
≤0.05 |
[dB] |
| 100 Turns Around a Mandrel of 25?mm?Radius |
1310nm and 1550nm |
≤0.05 |
[dB] |
|
| 1 Turn Around a Mandrel of 16?mm?Radius |
1550nm |
≤0.05 |
[dB] |
|
|
Coating Strip Force |
typical average force |
1.5 |
[N] |
|
|
peak force |
1.3-8.9 |
[N] |
||
| Dynamic Fatigue Parameter(nd) |
-- |
≥20 |
-- |
|